Standard: ASTM B622, ASTM B619, ASTM B626; Grade: Hastelloy B, Hastelloy B-2, Hastelloy B-3, Hastelloy C-4, Hastelloy S, Hastelloy G-30, Hastelloy G-35, Hastelloy C-2000, Hastelloy C22, Hastelloy C276; Size: Outside Diameter: Ø3.2-Ø219.1mm; Wall Thickness: 1.24-8.18mm; Application: Nuclear Fuel, Petrifaction, Fertilizers, Pesticides, Galvanizing Industry, Smog Cleaning, Thermal Power Plant, Airspace Engine, etc. |
Chemical Composition Wt.%
|
Hastelloy B (UNS N1001) |
Ni |
Si |
Cr |
Mo |
Fe |
V |
Co |
P |
C |
S |
Mn |
|
rest |
≤1.0 |
≤ 1.0 |
26 30 |
4 6 |
0.2 0.4 |
≤ 2.5 |
≤ 0.04 |
≤ 0.05 |
≤ 0.03 |
≤ 1.0 |
|
|
Hastelloy B-2 (UNS N10665) |
Ni |
Si |
Cr |
Mo |
Fe |
V |
Co |
P |
C |
S |
Mn |
|
rest |
≤0.1 |
≤ 1.0 |
26 30 |
0 2 |
0.2 0.4 |
≤ 1.0 |
≤ 0.04 |
≤ 0.02 |
≤ 0.03 |
≤ 1.0 |
|
|
Hastelloy B-3 (UNS N10675) |
Ni |
Cr |
Mo |
Fe |
W |
Co |
Cu |
C |
Al |
Mn |
Ti |
|
≥ 65 |
1 3 |
27 32 |
1 3 |
≤ 3 |
≤ 3 |
≤ 0.2 |
≤ 0.01 |
≤ 0.5 |
≤ 3 |
≤ 0.2 |
|
|
Si |
Nb |
V |
Ta |
P |
Zr |
S |
|
|
|
|
|
|
≤ 0.1 |
≤ 0.2 |
≤ 0.2 |
≤ 0.2 |
≤ 0.03 |
≤ 0.03 |
≤ 0.01 |
|
|
|
|
|
|
Hastelloy C22 (UNS N06022) |
Cr |
Mo |
Fe |
W |
Co |
V |
C |
Si |
Mn |
P |
S |
|
20 22.5 |
12.5 14.5 |
2 6 |
2.5 3.5 |
≤ 2.5 |
≤ 0.02 |
≤ 0.015 |
≤ 0.08 |
≤ 0.5 |
≤ 0.02 |
≤ 0.35 |
|
|
Hastelloy C-4 (UNS N06455) |
Ni |
Cr |
Mo |
Fe |
C |
Mn |
Co |
S |
P |
Ti |
Si |
|
rest |
14 18 |
14 17 |
0 3 |
≤ 0.015 |
≤ 1.0 |
≤ 2.0 |
≤ 0.03 |
≤ 0.04 |
≤ 0.7 |
≤ 0.08 |
|
|
Hastelloy S (UNS N06635) |
C |
Cr |
Mo |
W |
Al |
La |
Co |
Si |
Mn |
P |
S |
|
≤ 0.02 |
14.5 17 |
14 16.5 |
≤ 1.0 |
0.1 0.5 |
0.01 0.1 |
≤ 2.0 |
0.2 0.75 |
0.3 1 |
≤ 0.02 |
≤ 0.015 |
|
|
Hastelloy C276 (UNS N10276) |
Cr |
Mo |
Fe |
W |
Co |
C |
Mn |
Si |
V |
P |
S |
|
14.5 16.5 |
15 17 |
4 7 |
3 4.5 |
≤ 2.5 |
≤ 0.01 |
≤ 1 |
≤ 0.08 |
≤ 0.35 |
≤ 0.04 |
≤ 0.03 |
|
|
Hastelloy C-2000 (UNS N06200) |
Cr |
Mo |
Fe |
Al |
Co |
C |
Mn |
Si |
Cu |
P |
S |
|
22 24 |
15 17 |
≤ 3 |
≤ 0.5 |
≤ 2 |
≤ 0.01 |
≤ 0.5 |
≤ 0.08 |
1.3 1.9 |
≤ 0.025 |
≤ 0.01 |
|
|
Hastelloy G-35 (UNS N06035) |
Cr |
Mo |
Co |
W |
Mn |
Si |
P |
S |
Cu |
V |
Al |
|
32.25 34.25 |
7.6 9 |
≤ 1 |
≤ 0.6 |
≤ 0.5 |
≤ 0.6 |
≤ 0.03 |
≤ 0.015 |
≤ 0.3 |
≤ 0.2 |
≤ 0.4 |
|
|
Hastelloy G-30 (UNS N06030) |
Cr |
C |
Fe |
Mo |
W |
Cu |
Co |
Si |
Nb |
P |
S |
|
28 31.5 |
≤ 0.03 |
13 17 |
4 6 |
1.5 4 |
1 2.4 |
≤ 5 |
0.2 0.8 |
0.3 1.5 |
≤ 0.04 |
≤ 0.02 |
|
|
Hastelloy X (UNS N06002) |
Ni |
W |
Fe |
Mn |
C |
Si |
S |
Cr |
Mo |
P |
Co |
|
rest |
0.2 1 |
17 22 |
≤ 1 |
0.05 0.15 |
≤ 1 |
≤ 0.03 |
20.5 23 |
8 10 |
≤ 0.04 |
0.5 2.5 |
|
|
Hastelloy N (UNS N10003) |
C |
W |
Cr |
Mo |
Cu |
V |
Co |
P |
B |
S |
Mn |
|
0.04 0.08 |
≤ 0.5 |
6 8 |
15 18 |
≤ 0.35 |
≤ 0.5 |
≤ 0.2 |
≤ 0.015 |
≤ 0.01 |
≤ 0.02 |
≤ 1.0 |
|
|
Haynes 230 (UNS N06230) |
Cr |
Mo |
Al |
W |
Co |
B |
La |
Si |
Mn |
P |
S |
|
20 24 |
1 3 |
0.2 0.5 |
13 15 |
≤ 5 |
≤ 0.015 |
0.005 0.05 |
0.25 0.75 |
0.3 1 |
≤ 0.03 |
≤ 0.015 |
|
|
Haynes 556 (UNS R30556) |
Fe |
Cr |
Ni |
Co |
Mo |
W |
Mn |
Si |
C |
P |
S |
|
rest |
21 23 |
19 22.5 |
16 21 |
2.5 4 |
2 3.5 |
0.5 2.0 |
0.2 0.8 |
0.05 0.15 |
≤ 0.04 |
≤ 0.015 |
|
|
Al |
Zr |
La |
B |
Nb |
Ta |
N |
|
|
|
|
|
|
0.1 0.5 |
0.001 0.1 |
0.005 0.1 |
≤ 0.02 |
≤ 0.3 |
0.3 1.25 |
0.1 0.3 |
|
|
|
|
|
|
Haynes 188 (UNS R30188) |
Co |
Ni |
Cr |
W |
Fe |
Mn |
Si |
C |
La |
B |
|
|
rest |
22 |
22 |
14 |
≤3 |
≤1.25 |
0.35 |
0.1 |
0.03 |
≤0.015 |
|
Physical Constants
| Steel Grade |
Density (g/cm3) |
Melting Point ℃ |
Tensile Strength (Mpa) |
Yield Strength (Mpa) |
Elongation % |
|
Hastelloy B/B-2 |
9.24 |
1330-1380 |
690 |
310 |
40 |
|
Hastelloy B-3 |
9.24 |
1370-1418 |
760 |
350 |
40 |
|
Hastelloy C-22 |
8.94 |
1325-1370 |
690 |
283 |
40 |
|
Hastelloy C-4 |
8.94 |
1325-1370 |
650 |
280 |
40 |
|
Hastelloy S |
8.75 |
1335-1380 |
110 |
52 |
46 |
|
Hastelloy C276 |
8.9 |
1325-1370 |
690 |
283 |
40 |
|
Hastelloy C-2000 |
8.9 |
1335-1380 |
690 |
283 |
45 |
|
Hastelloy G-35 |
8.9 |
1332-1361 |
|
|
|
|
Hastelloy G-30 |
8.23 |
1335-1380 |
586 |
241 |
30 |
|
Hastelloy X |
8.28 |
1260-1335 |
660 |
240 |
35 |
|
Hastelloy N |
8.896 |
1300-1400 |
690 |
280 |
35 |
|
Haynes 230 |
8.97 |
1301-1371 |
758 |
310 |
40 |
|
Haynes 556 |
8.23 |
1330-1415 |
|
|
|
|
Haynes 188 |
8.89 |
1315-1410 |
|
|
|